Break Test (for tempered steel)

แปลว่า(english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges.

Black Oil Tempered Spring Steel Strip (Scaleless Blue)

แปลว่า(english) A flat cold rolled usually .70/.80 medium high carbon steel strip, blue-black in color, which has been quenched in oil and drawn to desired hardness. While it looks and acts much like blue tempered spring steel and carries a Rockwell hardness of C44/47, it has not been polished and is lower in carbon content. Used for less exacting requirements than clock spring steel, such as snaps, lock springs, hold down springs, trap springs, etc. It will take a more severe bend before fracture than will clock spring, but it does not have the same degree of spring-back.

Butcher Saw Steel

แปลว่า(english) A hardened, tempered, and polished high carbon spring steel strip material (carbon content is generally higher than that of a material used for wood band saw applications) with a Rockwell value of roughly C47/49.

Accordion Reed Steel

แปลว่า(english) Hardened, tempered, polished and blued or yellow flat steel with dressed edges. Carbon content about 1.00. Material has to possess good flatness, uniform hardness and high elasticity.

Bainite

แปลว่า(english) A eutectoid transformation product of ferrite and a fine dispersion of carbide, generally formed at temperatures below 840 to 930 F (450 to 500 C): upper bainite is an aggregate containing parallel lath-shape units of ferrite, produces the so-called feathery appearance in optical microscopy, and is formed at temperatures above about 660 F (350 C); lower bainite consists of individual plate-shape units and is formed at temperatures below about 660 F (350 C). Also, a slender, needle-like (acicular) microstructure appearing in spring steel strip characterized by toughness and greater ductility than tempered Martensite. Bainite is a decomposition product of Austenite best developed at interrupted holding temperatures below those forming fine pearlite and above those giving Martensite.

Band Saw Steel (Wood)

แปลว่า(english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45.