Blow Back

แปลว่า(english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film.

Condensation

แปลว่า(Concrete Engineering) When a moisture laden gas comes in contact with a cooler surface a change of state from gaseous to liquid occurs.

Anaerobic process

แปลว่า(Environmental Engineering) A process which only occurs in the absence of molecular oxygen.

Blush

แปลว่า(english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive.

Thermocline

แปลว่า(Environmental Engineering) The depth at which an inflection point occurs in a lake temperature profile.

Discrete settling

แปลว่า(Environmental Engineering) Settling in which individual particles settle independently, neither agglomerating or interfering with the settling of the other particles present. This occurs in waters with a low concentration of particles.

Bending Strength

แปลว่า(english) Upper limit of normal stress of a beam at which fracture or excessive plastic deformation occurs.

Nitrification

แปลว่า(Environmental Engineering) The biological oxidation of ammonia and ammonium sequentially to nitrite and then nitrate. It occurs naturally in surface waters, and can be engineered in wastewater treatment systems. The purpose of nitrification in wastewater treatment systems is a reduction in the oxygen demand resulting from the ammonia.

Risk

แปลว่า(Software Engineering) a potential problem or occurrence that put a project in jeopardy ความเสี่ยง

Business risks

แปลว่า(Software Engineering) the set of potential business problems or occurrences that may cause the project to fail

Blue Brittleness 2

แปลว่า(english) Reduced ductility occurring as a result of strain aging, when certain ferrous alloys are worked between 300 and 700 (degrees) F. This phenomenon may be observed at the working temperature or subsequently at lower temperatures.

Aging 2

แปลว่า(english) A change in properties that occurs at ambient or moderately elevated temperatures after hot working or a heat treating operation (quench aging in ferrous alloys), or after a cold working operation (strain aging). The change in properties is often, but not always, due to a phase change (precipitation), but does not involve a change in chemical composition. In a metal or alloy, a change in properties that generally occurs slowly at room temperature and more rapidly at higher temperatures.