ผลการค้นหา

Rock Pocket

แปลว่า(Concrete Engineering) Area or portion of hardened concrete which is deficient in mortar and consisting primarily of coarse aggregate and open voids; caused by insufficient consolidation or separation during placement, or both; by leakage from form.

Break Test (for tempered steel)

แปลว่า(english) A method of testing hardened and tempered high carbon spring steel strip wherein the specimen is held and bent across the grain in a vice-like calibrated testing machine. Pressure is applied until the metal fractures at which point a reading is taken and compared with a standard chart of brake limitations for various thickness ranges.

Butcher Saw Steel

แปลว่า(english) A hardened, tempered, and polished high carbon spring steel strip material (carbon content is generally higher than that of a material used for wood band saw applications) with a Rockwell value of roughly C47/49.

Brinell Hardness Testing

แปลว่า(english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function.

Pretensioning

แปลว่า(Concrete Engineering) A method of prestressing reinforced concrete in which the steel is stressed before the concrete has hardened and restrained from gaining its unstressed position by bond to the concrete.

hardened steel roller

แปลว่าขดเหล็กรูปทรงกระบอกของแหนบรองรับน้ำหนักรถ

Burnishing 2

แปลว่า(english) Smoothing surfaces through friction between the material and material such as hardened metal media.

Agglomerating Processes

แปลว่า(english) "Fine particles of limestone (flux) and iron ore are difficult to handle and transport because of dusting and decomposition, so the powdery material usually is processed into larger pieces. The raw material's properties determine the technique that is used by mills. 1) SINTER Baked particles that stick together in roughly one-inch chunks. Normally used for iron ore dust collected from the blast furnaces. 2) PELLETS Iron ore or limestone particles are rolled into little balls in a balling drum and hardened by heat. 3) BRIQUETTES Small lumps are formed by pressing material together. Hot Iron Briquetting (HBI) is a concentrated iron ore substitute for scrap for use in electric furnaces.

Accordion Reed Steel

แปลว่า(english) Hardened, tempered, polished and blued or yellow flat steel with dressed edges. Carbon content about 1.00. Material has to possess good flatness, uniform hardness and high elasticity.

Carbonation

แปลว่า(Concrete Engineering) 1) Reaction between the products of portland cement (soluble calcium hydroxides), water and carbon dioxide to produce insoluble calcium carbonate (efflorescence). 2) Soft white, chalky surface dusting of freshly placed, unhardened concrete caused by carbon dioxide from unvented heaters or gasoline powered equipment in an enclosed space. 3) Carbonated, dense, impermeable to absorption, top layer of the surface of concrete caused by surface reaction to carbon dioxide. This carbonated layer becomes denser and deeper over a period of time. 4) Reaction with carbon dioxide which produces a slight shrinkage in concrete. Improves chemical stability. Concrete masonry units during manufacturing may be deliberately exposed to carbon dioxide after reaching 80% strength to induce carbonation shrinkage to make the units more dimensionally stable. Future drying shrinkage is reduced by as much as 30%.

Band Saw Steel (Wood)

แปลว่า(english) A hardened tempered bright polished high carbon cold rolled spring steel strip produced especially for use in the manufacture of band saws for sawing wood, non ferrous metals, and plastics. Usually carries some nickel and with a Rockwell value of approximately C40/45.

Brinell Hardness Test

แปลว่า(english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula.