Acid Process 2

แปลว่า(english) A steel making method using an acid refractory-lined (usually silica) furnace. Neither sulfur or phosphorus is removed.

Blow Back

แปลว่า(english) A coating defect consisting of a lower coating film weight on the bottom of the coated sheet caused by high velocity air in the oven. Blow back usually occurs with high solids coatings which have little solvent to evaporate and "set" the film.

Bearing Load

แปลว่า(english) A compressive load supported by a member, usually a tube or collar, along a line where contact is made with a pin, rivet, axle, or shaft.

Billet

แปลว่า(english) (1) A semi-finished section hot rolled from a metal ingot, with a rectangular cross section usually ranging from 16 to 36 in., the width being less than twice the thickness. Where the cross section exceeds 36 in., the term “bloom” is properly but not universally used. Sizes smaller than 16 in. are usually termed “bars”; a solid semi-finished round or square product which has been hot worked by forging, rolling, or extrusion. (2) A semi-finished, cogged, hot rolled or continuous-cast metal product of uniform section, usually rectangular with radiused corners. Billets are relatively larger than bars.

Bell Mouth

แปลว่า(english) The flaring or tapering of a machined hole, usually made at the entrance end because of misalignment or spring of the cutting tool.

Blush

แปลว่า(english) A coating defect consisting of the whitening of a cured film which results in a translucent or opaque appearance with accompanying loss of gloss. Blushing usually occurs during the pasteurization or steam processing of films which are undercured or water sensitive.

BLADDER

แปลว่า(english) A separator or diaphragm usually found in a chamber to facilitate separation of two (2) fluids or gases.

Black Oil Tempered Spring Steel Strip (Scaleless Blue)

แปลว่า(english) A flat cold rolled usually .70/.80 medium high carbon steel strip, blue-black in color, which has been quenched in oil and drawn to desired hardness. While it looks and acts much like blue tempered spring steel and carries a Rockwell hardness of C44/47, it has not been polished and is lower in carbon content. Used for less exacting requirements than clock spring steel, such as snaps, lock springs, hold down springs, trap springs, etc. It will take a more severe bend before fracture than will clock spring, but it does not have the same degree of spring-back.

Bloom 2

แปลว่า(english) A semi-finished hot rolled product, rectangular in cross section, produced on a blooming mill. For iron and steel, the width is not more than twice the thickness, and the cross-sectional area is usually not less than 36 sq. in. Iron and steel blooms are sometimes made by forging.

Box Annealing

แปลว่า(english) Annealing a metal or alloy in a sealed container under conditions that minimize oxidation. In box annealing a ferrous alloy, the charge is usually heated slowly to a temperature below the transformation range, but sometimes above or within it, and is then cooled slowly; this process is also called close annealing or pot annealing.

Tilt-up

แปลว่า(Concrete Engineering) A method of concrete construction such as where members are cast horizontally near their eventual position, usually on a recently placed slab, and then tilted into place after removal of forms.

Pin support:

แปลว่า(english) In two dimensions, a pin support restrains two translation degrees of freedom but does not restrain rotation. When considering reaction forces, a pin support is usually considered to have two force components: one each about the x and y axes respectively.