Brinell Hardness Testing

แปลว่า(english) Method of determining the hardness of materials; involves impressing a hardened ball of specified diameter into the material surface at a known pressure (10-mm ball, 500-kg load for aluminum alloys). The Brinell hardness number results from calculations involving the load and the spherical area of the ball impression. Direct-reading testing are generally used for routine inspection of forgings, and as a heat treat control function.

Brinell Hardness

แปลว่า(english) The hardness of a metal or part, as represented by the number obtained from the ratio between the load applied on the spherical area of the impression made by a steel ball forced into the surface of the material tested.

Brinell Hardness Test

แปลว่า(english) A common standard method of measuring the hardness of materials. The smooth surface of the metal is subjected to indentation by a hardened steel ball under pressure. The diameter of the indentation, in the material surface, is then measured by a microscope and the hardness value is read from a chart or determined by a prescribed formula.

Brinell Hardness Number

แปลว่า(english) The value of hardness of a metal on an arbitrary scale representing kg/mm2, determined by measuring the diameter of the impression made by a ball of given diameter applied under a known load. Values are expressed in Brinell Hardness Numbers, BHN

Boron (chemical symbol B)

แปลว่า(english) Element N. 5 of the periodic system. Atomic weight 10.82. It is gray in color, ignites at about 1112 (degrees) F. and burns with a brilliant green flame, but its melting point in a non-oxidizing atmosphere is about 4000 (degrees) F. Boron is used in steel in minute quantities for one purpose only- to increase the hardenability as in case hardening and to increase strength and hardness penetration.

Black Oil Tempered Spring Steel Strip (Scaleless Blue)

แปลว่า(english) A flat cold rolled usually .70/.80 medium high carbon steel strip, blue-black in color, which has been quenched in oil and drawn to desired hardness. While it looks and acts much like blue tempered spring steel and carries a Rockwell hardness of C44/47, it has not been polished and is lower in carbon content. Used for less exacting requirements than clock spring steel, such as snaps, lock springs, hold down springs, trap springs, etc. It will take a more severe bend before fracture than will clock spring, but it does not have the same degree of spring-back.

Beryllium Copper

แปลว่า(english) An alloy of copper and 2-3% beryllium with optionally fractional percentages of nickel or cobalt. Alloys of this series show remarkable age-hardening properties and an ultimate hardness of about 400 Brinell (Rockwell C43). Because of such hardness and good electrical conductivity, beryllium-copper is used in electrical switches, springs, etc.

Brown Sharp Gages

แปลว่า(english) A standard series of sizes refered to by numbers, in which the diameter of wire or thickness of sheet metal is generally produced and which is used in the manufacture of brass, bronze, copper, copper-base alloys and aluminum. These gage numbers have a definite relationship to each other. In this system, the decimal thickness is reduced by 50% every six gage numbers- while temper is expressed by the number of B&S gage numbers as cold reduced in thickness from previous annealing. For each B&S gage number in thickness reduction, where is assigned a hardness value of 1/4 hard.

Brale

แปลว่า(english) A diamond penetrator, conical in shape, used with a Rockwell hardness tester for hard metals.

Accordion Reed Steel

แปลว่า(english) Hardened, tempered, polished and blued or yellow flat steel with dressed edges. Carbon content about 1.00. Material has to possess good flatness, uniform hardness and high elasticity.

Age Hardening

แปลว่า(english) Hardening by aging, usually after rapid cooling or cold working. The term as applied to soft, or low carbon steels, relates to a wide variety of commercially important, slow, gradual changes that take place in properties of steels after the final treatment. These changes, which bring about a condition of increased hardness, elastic limit, and tensile strength with a consequent loss in ductility, occur during the period in which the steel is at normal temperatures.

Magnetite

แปลว่า(Concrete Engineering) An aggregate used in heavy weight concrete, consisting primarily of ferrous metaferrite (Fe304). A black magnetic iron ore with a specific gravity of approximately 5.2 and a Mohs hardness of about 6.